INFINO® NE-1030TV

Technical Documents

INFINO® NE-1030TV is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy. Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polycarbonate

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • high impact strength & modulus
  • high flowability
  • good colorability
  • excellent appearance
  • well-balanced mechanical properties & processability
  • halogen free
  • flame retardant
Other Applications

Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Humidity <0.04 %
MFI 25 g/10min ISO 1133;250℃/2.16kg
MFI 75 g/10min ISO 1133;220℃/10kg
Shrinkage 0.06 % (ISO 2577;Cross Flow, 3.2 mm (TD
Shrinkage 0.06 % (ISO 2577;Flow, 3.2 mm (MD
Density 1.2 g/ml ISO 1183
Thermal Properties
Heat Deflection temperature 66 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Dry Time 180 - 240 min
UL RTI 60 ºC Mechanical without Impact, 1.5 mm, 2.5 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 1.5 mm, 2.5 mm, 3.0 mm
UL RTI 60 ºC Electric, 1.5 mm, 2.5 mm, 3.0 mm
Vicat softening temperature 87 ºC ISO R 306;B/50
Heat Deflection temperature 68 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Pencil Hardness H JIS K 5401;500 g
Rockwell Hardness 116 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 20 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 25 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 2400 MPa ISO 178;2mm/min
Flexural strength 85 MPa ISO 178;2mm/min
Tensile Stress at break-MD 55 MPa ISO 527;50mm/min
Tensile modulus-MD 2200 MPa ISO 527;50mm/min
Strain at break-MD 60 % ISO 527;50mm/min
Tensile Stress at yield-MD 55 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >400 ºC