INFINO® NH-1037 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Shrinkage | 0.5 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
Humidity | <0.05 | % | |
Density | 1.18 | g/ml | ISO 1183 |
MFI | 20 | g/10min | ISO 1133;250℃/10kg |
Thermal Properties | |||
Vicat softening temperature | 114 | ºC | ISO R 306;B/120 |
Heat Deflection temperature | 106 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 100 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 105 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Dry Time | 240 - 360 | min | |
Dry Time | 120 - 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 2.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 2.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.5 mm, 2.5 mm, 3.0 mm |
Vicat softening temperature | 111 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 93 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 120 | ISO 2039-2;R Scale | |
(Izod impact strength(notched | 32 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Charpy Impact Strength (notched) | 36 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
Flexural modulus-MD | 2500 | MPa | ISO 178;2mm/min |
Flexural strength | 92 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 55 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2400 | MPa | ISO 527;50mm/min |
Strain at break-MD | 28 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 61 | MPa | ISO 527;50mm/min |