INFINO® NH-1037 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.
Детали
Тип продукта
Промышленность
Режиссер
Дреимущества
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Другие приложения
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Физические свойства | |||
| Shrinkage | 0.5 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| Density | 1.18 | g/ml | ISO 1183 |
| MFI | 20 | g/10min | ISO 1133;250℃/10kg |
| Тепловые свойства | |||
| Vicat softening temperature | 114 | ºC | ISO R 306;B/120 |
| Heat Deflection temperature | 106 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 100 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 105 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Dry Time | 240 - 360 | min | |
| Dry Time | 120 - 240 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 2.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 2.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 2.5 mm, 3.0 mm |
| Vicat softening temperature | 111 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 93 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Механические свойства | |||
| Rockwell Hardness | 120 | ISO 2039-2;R Scale | |
| (Izod impact strength(notched | 32 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Charpy Impact Strength (notched) | 36 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| Flexural modulus-MD | 2500 | MPa | ISO 178;2mm/min |
| Flexural strength | 92 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 55 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2400 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 28 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 61 | MPa | ISO 527;50mm/min |