INFINO® NH-1101

INFINO® NH-1101 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polycarbonate

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • high impact strength & modulus
  • high flowability
  • good colorability
  • excellent appearance
  • well-balanced mechanical properties & processability
  • halogen free
  • flame retardant
Other Applications

Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter

Technical data

Quantity Value Unit Comment
Appearance Properties
Appearance Natural colors
Physical state Pill
Physical Properties
Humidity <0.05 %
MFI 27 g/10min ISO 1133;220℃/10kg
Density 1.22 g/ml ISO 1183
Thermal Properties
Auto-ignition temperature >700 ºC
Heat Deflection temperature 94 ºC ISO 75-2;0.45 MPa, 4.0 mm, Annealing
Heat Deflection temperature 87 ºC ISO 75-2;1.8 MPa, 4.0 mm, Annealing
Heat Deflection temperature 91 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Dry Time 240 - 360 min
Dry Time 120 - 240 min
UL RTI 60 ºC Mechanical without Impact, 1.2 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 1.2 mm, 3.0 mm
UL RTI 60 ºC Electric, 1.2 mm, 3.0 mm
Vicat softening temperature 98 ºC ISO R 306;B/120
Vicat softening temperature 96 ºC ISO R 306;B/50
Heat Deflection temperature 81 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 114 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 13 kJ/m² ISO 179 1eA;at 23°C, 4 mm
(Izod impact strength(notched 8 kJ/m² ISO 180 1A;at 23°C, 4 mm
Flexural modulus-MD 3300 MPa ISO 178;2.8mm/min
Flexural strength 93 MPa ISO 178;2.8mm/min
Tensile Stress at break-MD 33 MPa ISO 527;50mm/min
Tensile modulus-MD 3300 MPa ISO 527;50mm/min
Strain at break-MD 29 % ISO 527;50mm/min
Tensile Stress at yield-MD 61 MPa ISO 527;50mm/min
Chemical Properties
Decomposition temperature >379 ºC