myINFINO® NH-1101 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.
Детали
Тип продукта
Промышленность
Режиссер
Дреимущества
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Другие приложения
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Физические свойства | |||
| Humidity | <0.05 | % | |
| MFI | 27 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.22 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| Auto-ignition temperature | >700 | ºC | |
| Heat Deflection temperature | 94 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 87 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 91 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Dry Time | 240 - 360 | min | |
| Dry Time | 120 - 240 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.2 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.2 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.2 mm, 3.0 mm |
| Vicat softening temperature | 98 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 96 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 81 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Механические свойства | |||
| Rockwell Hardness | 114 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 13 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 8 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 3300 | MPa | ISO 178;2.8mm/min |
| Flexural strength | 93 | MPa | ISO 178;2.8mm/min |
| Tensile Stress at break-MD | 33 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 3300 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 29 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 61 | MPa | ISO 527;50mm/min |
| Химические свойства | |||
| Decomposition temperature | >379 | ºC | |