myInjection Molding, PC/ABS, Halogen Free Flame Retardant, Heat Resistance, High Flow
Details
CAS
9003-56-9
Applications
Producer
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Specific Gravity | 1.18 | ||
| Humidity | <2 | % | |
| Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
| MFI | 18 | g/10min | 250°C/2.16Kg |
| Thermal Properties | |||
| Flameability | Thickness 2- mm | ||
| Flameability | Thickness 3- mm | ||
| Flameability | Thickness 1.5- mm | ||
| Flameability | Thickness 3- mm | ||
| Flameability | Thickness 1- mm | ||
| Flameability | Thickness 2- mm | ||
| Flameability | Thickness 1.5- mm | ||
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 3- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 2- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 3- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 2- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 3- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 2- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 1- mm |
| Dry Time | 180 - 300 | min | |
| Mechanical Properties | |||
| Rockwell Hardness | 113 | ||
| Izod impact strength (notched) | J/m | Thickness 3.2 mm | |
| Flexural modulus-MD | 2451.66 | MPa | Thickness 6.4 mm |
| Flexural strength | 84.33 | MPa | Thickness 6.4 mm |
| Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
| Elongation at break-MD | 50 | % | Thickness 3.2 mm |
| Process Properties | |||
| Middle Barrel Temperature | 235 - 255 | ºC | |
| Mold Temperature | 50 - 80 | ºC | |
| Drying Temperature | 75 - 85 | ºC | |