myInjection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame Retardant
Details
CAS
9003-56-9
Applications
Producer
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| MFI | 7 | g/10min | 250°C/2.16Kg |
| Linear Mold Shrinkage | 0.003 - 0.005 | cm/cm | Thickness 3.2 mm |
| Specific Gravity | 1.21 | ||
| Humidity | <4 | % | |
| Thermal Properties | |||
| UL RTI | 60 | ºC | Electrical-Thickness 0.75- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 3- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 0.75- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 3- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 0.75- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 3- mm |
| Flameability | Thickness 0.75- mm | ||
| Heat Deflection temperature | 96 | ºC | |
| Flameability | Thickness 3- mm | ||
| Flameability | Thickness1.5- mm | ||
| Dry Time | 240 - 360 | min | |
| Mechanical Properties | |||
| Tensile strength | 57.85 | MPa | Thickness 3.2 mm |
| Flexural strength | 96.10 | MPa | Thickness 6.4 mm |
| Flexural modulus-MD | 3040.06 | MPa | Thickness 6.4 mm |
| Izod impact strength (notched) | 245 | J/m | Thickness 3.2 mm |
| Elongation at break-MD | >50 | % | Thickness 3.2 mm |
| Process Properties | |||
| Drying Temperature | 75 - 85 | ºC | |
| Mold Temperature | 50 - 80 | ºC | |
| Middle Barrel Temperature | 235 - 255 | ºC | |