Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame Retardant
Детали
CAS
9003-56-9
Режиссер
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
MFI | 7 | g/10min | 250°C/2.16Kg |
Linear Mold Shrinkage | 0.003 - 0.005 | cm/cm | Thickness 3.2 mm |
Specific Gravity | 1.21 | ||
Humidity | <4 | % | |
Тепловые свойства | |||
UL RTI | 60 | ºC | Electrical-Thickness 0.75- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.5- mm |
UL RTI | 60 | ºC | Electrical-Thickness 3- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 0.75- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 3- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 0.75- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 3- mm |
Flameability | Thickness 0.75- mm | ||
Heat Deflection temperature | 96 | ºC | |
Flameability | Thickness 3- mm | ||
Flameability | Thickness1.5- mm | ||
Dry Time | 240 - 360 | min | |
Механические свойства | |||
Tensile strength | 57.85 | MPa | Thickness 3.2 mm |
Flexural strength | 96.10 | MPa | Thickness 6.4 mm |
Flexural modulus-MD | 3040.06 | MPa | Thickness 6.4 mm |
Izod impact strength (notched) | 245 | J/m | Thickness 3.2 mm |
Elongation at break-MD | >50 | % | Thickness 3.2 mm |
Свойства процесса | |||
Drying Temperature | 75 - 85 | ºC | |
Mold Temperature | 50 - 80 | ºC | |
Middle Barrel Temperature | 235 - 255 | ºC |