Injection Molding, PC/ABS, Halogen Free Flame Retardant, General PurposeApplication
Details
CAS
9003-56-9
Applications
Producer
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Humidity | <2 | % | injection molding |
Specific Gravity | 1.18 | ||
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
MFI | 9.5 | g/10min | 250°C/2.16Kg |
Thermal Properties | |||
Flameability | Thickness 2.5- mm | ||
Flameability | Thickness 3- mm | ||
Flameability | Thickness 2- mm | ||
Flameability | Thickness 1.5- mm | ||
Flameability | Thickness 2.5- mm | ||
Flameability | Thickness 3- mm | ||
Flameability | Thickness 1.5- mm | ||
Flameability | Thickness 2- mm | ||
Flameability | Thickness 1.2- mm | ||
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 3- mm |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 2.5- mm |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 2- mm |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.2- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 3- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 2.5- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 2- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.2- mm |
UL RTI | 80 | ºC | Electrical-Thickness 3- mm |
UL RTI | 80 | ºC | Electrical-Thickness 2.5- mm |
UL RTI | 80 | ºC | Electrical-Thickness 2- mm |
UL RTI | 80 | ºC | Electrical-Thickness 1.5- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.2- mm |
Dry Time | 240 - 360 | min | |
Mechanical Properties | |||
Izod impact strength (notched) | 490 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2353.59 | MPa | Thickness 6.4 mm |
Flexural strength | 86.29 | MPa | Thickness 6.4 mm |
Tensile strength | 54.91 | MPa | Thickness 3.2 mm |
Elongation at break-MD | >50 | % | Thickness 3.2 mm |
Electrical Properties | |||
HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 1.5 mm |
Arc Resistance | 60 - 120 | s | |
Hot Wire Ignition | 30 - 60 | s | Thickness 2- mm |
Hot Wire Ignition | 30 - 60 | s | Thickness 1.5- mm |
Hot Wire Ignition | 30 - 60 | s | Thickness 1.2- mm |
HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 2 mm |
Comparative Tracking Index | 250 - 400 | V | |
Process Properties | |||
Middle Barrel Temperature | 230 - 260 | ºC | |
Mold Temperature | 50 - 70 | ºC | |
Drying Temperature | 60 - 80 | ºC |