myاین پلیمر، تاخیر دهنده ی شعله است و گرید قالب گیری تزریقی می باشد.
جزئیات
CAS
9003-56-9
حوزه کاربردی
تولید کننده
داده های فنی
| کمیت | مقدار | واحد | توضیحات |
|---|---|---|---|
| خواص فیزیکی | |||
| Humidity | <2 | % | injection molding |
| Specific Gravity | 1.18 | ||
| Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
| MFI | 9.5 | g/10min | 250°C/2.16Kg |
| خواص حرارتی | |||
| Flameability | 5VA | Thickness 2.5- mm | |
| Flameability | 5VA | Thickness 3- mm | |
| Flameability | 5VA | Thickness 2- mm | |
| Flameability | 5VA | Thickness 1.5- mm | |
| Flameability | V-0 | Thickness 2.5- mm | |
| Flameability | V-0 | Thickness 3- mm | |
| Flameability | V-0 | Thickness 1.5- mm | |
| Flameability | V-0 | Thickness 2- mm | |
| Flameability | V-0 | Thickness 1.2- mm | |
| UL RTI | 85 | ºC | Mechanical without Impact-Thickness 3- mm |
| UL RTI | 85 | ºC | Mechanical without Impact-Thickness 2.5- mm |
| UL RTI | 85 | ºC | Mechanical without Impact-Thickness 2- mm |
| UL RTI | 85 | ºC | Mechanical without Impact-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.2- mm |
| UL RTI | 80 | ºC | Mechanical with Impact-Thickness 3- mm |
| UL RTI | 80 | ºC | Mechanical with Impact-Thickness 2.5- mm |
| UL RTI | 80 | ºC | Mechanical with Impact-Thickness 2- mm |
| UL RTI | 80 | ºC | Mechanical with Impact-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.2- mm |
| UL RTI | 80 | ºC | Electrical-Thickness 3- mm |
| UL RTI | 80 | ºC | Electrical-Thickness 2.5- mm |
| UL RTI | 80 | ºC | Electrical-Thickness 2- mm |
| UL RTI | 80 | ºC | Electrical-Thickness 1.5- mm |
| UL RTI | 60 | ºC | Electrical-Thickness 1.2- mm |
| Dry Time | 240 - 360 | min | |
| خواص مکانیکی | |||
| Izod impact strength (notched) | 490 | J/m | Thickness 3.2 mm |
| Flexural modulus-MD | 2353.59 | MPa | Thickness 6.4 mm |
| Flexural strength | 86.29 | MPa | Thickness 6.4 mm |
| Tensile strength | 54.91 | MPa | Thickness 3.2 mm |
| Elongation at break-MD | >50 | % | Thickness 3.2 mm |
| خواص الکتریکی | |||
| HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 1.5 mm |
| Arc Resistance | 60 - 120 | s | |
| Hot Wire Ignition | 30 - 60 | s | Thickness 2- mm |
| Hot Wire Ignition | 30 - 60 | s | Thickness 1.5- mm |
| Hot Wire Ignition | 30 - 60 | s | Thickness 1.2- mm |
| HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 2 mm |
| Comparative Tracking Index | 250 - 400 | V | |
| خواص فرایندی | |||
| Middle Barrel Temperature | 230 - 260 | ºC | |
| Mold Temperature | 50 - 70 | ºC | |
| Drying Temperature | 60 - 80 | ºC | |