starex® GC-0703

starex® GC-0703 is an eco-friendly acrylonitrile butadiene styrene (ABS) and polyethylene terephthalate (PET) grade based on 15 % post-consumer materials (PCM).Can be processed using injection molding.

Details

Product Type

Polymer > ABS
Polymer > Polyesters

Applications

Polymers industry > Injection moulding

Industry

Electronics

Producer

Samsung

Advantages
  • helps in reduction of carbon emission
  • good chemical resistance
  • well balanced properties
  • eco-friendly
Other Applications

Automotive
Electronics / Computers > Monitors, OA machines
Telecom > Cellular phones

Handling

It complies with the EPEAT Gold & TCO Edge eco-certifications, and RoHS regulation.

Technical data

Quantity Value Unit Comment
Appearance Properties
Physical state Pill
Appearance Natural colors
Physical Properties
Shrinkage 0.3 - 0.8 % (ISO 2577;Cross flow, 3.2 mm (TD
Shrinkage 0.3 - 0.8 % (ISO 2577;Flow, 3.2 mm (MD
Humidity <0.02 %
Density 1.07 g/ml ISO 1183
Thermal Properties
Auto-ignition temperature >400 ºC
Dry Time 240 min
UL RTI 60 ºC Mechanical without Impact, 1.5 mm, 3.0 mm
UL RTI 60 ºC Electric, 1.5 mm, 3.0 mm
UL RTI 60 ºC Mechanical with Impact, 1.5 mm, 3.0 mm
Vicat softening temperature 91 ºC ISO R 306;B/50
Heat Deflection temperature 80 ºC ISO 75-2;0.45 MPa, 4.0 mm, Unannealed
Heat Deflection temperature 70 ºC ISO 75-2;1.8 MPa, 4.0 mm, Unannealed
Mechanical Properties
Rockwell Hardness 94 ISO 2039-2;R Scale
Charpy Impact Strength (notched) 15 kJ/m² ISO 179 1eA;at 23°C, 4 mm
Tensile Stress at yield-MD 40 MPa ISO 527;50mm/min
Strain at break-MD 14 % ISO 527;50mm/min
Tensile modulus-MD 1650 MPa ISO 527;50mm/min
Tensile Stress at break-MD 35 MPa ISO 527;50mm/min
Flexural strength 50 MPa ISO 178;2mm/min
Flexural modulus-MD 1900 MPa ISO 178;2mm/min
(Izod impact strength(notched 15 kJ/m² ISO 180 1A;at 23°C, 4 mm
Chemical Properties
Decomposition temperature >300 ºC