starex® GC-0703 is an eco-friendly acrylonitrile butadiene styrene (ABS) and polyethylene terephthalate (PET) grade based on 15 % post-consumer materials (PCM).Can be processed using injection molding.
Детали
Тип продукта
Промышленность
Режиссер
Дреимущества
- helps in reduction of carbon emission
- good chemical resistance
- well balanced properties
- eco-friendly
Другие приложения
Automotive
Electronics / Computers > Monitors, OA machines
Telecom > Cellular phones
Обработка
It complies with the EPEAT Gold & TCO Edge eco-certifications, and RoHS regulation.
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Свойства внешнего вида | |||
Physical state | Pill | ||
Appearance | Natural colors | ||
Физические свойства | |||
Shrinkage | 0.3 - 0.8 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
Shrinkage | 0.3 - 0.8 | % | (ISO 2577;Flow, 3.2 mm (MD |
Humidity | <0.02 | % | |
Density | 1.07 | g/ml | ISO 1183 |
Тепловые свойства | |||
Auto-ignition temperature | >400 | ºC | |
Dry Time | 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
Vicat softening temperature | 91 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 80 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 70 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Механические свойства | |||
Rockwell Hardness | 94 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 15 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
Tensile Stress at yield-MD | 40 | MPa | ISO 527;50mm/min |
Strain at break-MD | 14 | % | ISO 527;50mm/min |
Tensile modulus-MD | 1650 | MPa | ISO 527;50mm/min |
Tensile Stress at break-MD | 35 | MPa | ISO 527;50mm/min |
Flexural strength | 50 | MPa | ISO 178;2mm/min |
Flexural modulus-MD | 1900 | MPa | ISO 178;2mm/min |
(Izod impact strength(notched | 15 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Химические свойства | |||
Decomposition temperature | >300 | ºC |