VESTAMID® LX9102 is a specially modified electrically conductive nylon 12 for use in conductive multilayer tubing.
Details Compound
Product Type
Producer
Supplier
Advantages
- d electrically conductive
- a lower melt viscosity
- excellent extrudability also in thin layer
- excellent quality of the inner surface
- avoid electrostatic charging generated by fuel flow
Other Applications
multilayer tubing MLT 140.2 and MLT 2040.2
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.12 | g/ml | ISO 1183 |
| Shrinkage | 1.4 | % | ISO 294-4,2577; parallel |
| Shrinkage | 1.5 | % | ISO 294-4,2577; normal |
| Thermal Properties | |||
| Heat Deflection temperature | 120 | ºC | ISO 75-1/-2;at 0.45 MPa |
| Heat Deflection temperature | 55 | ºC | ISO 75-1/-2;at 1.8 MPa |
| Dry Time | 480 - 960 | min | |
| Flameability | IEC 60695-11-10@Thickness 1.60 mm | ||
| Vicat softening temperature | 136 | ºC | 50°C/hr/50 N; ISO 306 |
| Flameability | IEC 60695-11-10@Thickness 3.2 mm | ||
| Melting point | 171 | ºC | 10°C/min; ISO 11357-1/-3 |
| Mechanical Properties | |||
| Tensile modulus-MD | 640 | MPa | ISO 527-1/-2 |
| Yield Stress -MD | 32 | MPa | ISO 527-1/-2 |
| Elongation at yield | 37 | % | ISO 527-1/-2 |
| Charpy Impact Strength (notched) | 5 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Strain at break-MD | >50 | % | ISO 527-1/-2 |
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
| Charpy Impact Strength (notched) | 90 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C;Partial break |
| Chemical Properties | |||
| Water absorption | 1.5 | % | Sim. to ISO 62 |
| Moisture absorption | 0.5 | % | Sim. to ISO 62 |
| Electrical Properties | |||
| Volume resistance | 100 | ohm-cm | IEC 60093 |
| Process Properties | |||
| Drying Temperature | 80 | ºC | |