Density |
1.26 |
g/ml |
ISO 1183 |
Linear Mold Shrinkage |
0.014 |
cm/cm |
Pigmentation can change mold shrinkage. |
Linear Mold Shrinkage |
0.014 |
cm/cm |
Pigmentation can change mold shrinkage.;Transverse |
MFI |
15.12 |
g/10min |
ISO 1133@Load 2.16 kg, Temperature 250 °C |
Melting range |
200 - 205 |
ºC |
DSC |
Thermal Expansion |
150 |
µm/m-°C |
Longitudinal; ISO 11359@Temperature 23.0 - 55.0 °C |
Thermal Expansion |
150 |
µm/m-°C |
ISO 11359@Temperature 23.0 - 55.0 °C; Transverse to Flow |
Heat Deflection temperature |
110 |
ºC |
ISO 75-1/2;at 0.46 MPa |
Heat Deflection temperature |
50.0 |
ºC |
ISO 75-1/2;at 1.8 MPa |
Vicat softening temperature |
125 |
ºC |
50N; ISO 306 |
Vicat softening temperature |
190 |
ºC |
10N; ISO 306 |
Flameability |
|
|
@Thickness 0.800 mm |
Flameability |
|
|
@Thickness 1.60 mm |
Hardness Shore D |
65 |
|
ISO 868 |
Ball indentation Hardness |
50.0 |
MPa |
H30; ISO 2039-1 |
Tensile Stress at yield-MD |
27.0 |
MPa |
50 mm/min; ISO 527-1/2 |
Elongation at break-MD |
>50 |
% |
50 mm/min; ISO 527-1/2 |
Tensile modulus-MD |
550 |
MPa |
ISO 527-1/2 |
(Charpy Impact Strength(unnotched |
|
kJ/m² |
ISO 179/1eU@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched |
|
kJ/m² |
ISO 179/1eU@Temperature -30.0 °C |
Charpy Impact Strength (notched) |
30 |
kJ/m² |
ISO 179/1eA@Temperature 23.0 °C |
Charpy Impact Strength (notched) |
8 |
kJ/m² |
ISO 179/1eA@Temperature -30.0 °C |
Elongation at yield |
23 |
% |
50 mm/min; ISO 527-1/2 |
Water absorption |
0.35 |
% |
ISO 62;at Saturation |
Oxirane Oxygen Content |
20 |
% |
ISO 4589 |
Electrolytic Corrosion |
|
|
IEC 60426 |
Comparative Tracking Index |
600 |
V |
Test Solution A, CTI; IEC 60112 |
Comparative Tracking Index |
575 |
V |
Test Solution A, 100 drops; IEC 60112 |
Dielectric Strength |
27.0 |
Kv/mm |
K20/P50; IEC 60243-1 |
Dissipation Factor |
0.033 |
|
IEC 60250@Frequency 1e+6 Hz |
Dissipation Factor |
0.022 |
|
IEC 60250@Frequency 100 Hz |
Dielectric Constant |
3.6 |
|
IEC 60250@Frequency 1e+6 Hz |
Dielectric Constant |
4.0 |
|
IEC 60250@Frequency 100 Hz |
Surface Resistance |
1.00e+13 |
ohm |
IEC 60093 |
Volume resistance |
1.00e+15 |
ohm-cm |
IEC 60093 |