PLEXIGLAS® Resist zk6HF is an amorphous, impact-modified thermoplastic molding compound (PMMA-I). .Application: Used for injection molding as well as for extruding sheets and profiles.
Details
Product Type
Applications
Producer
Supplier
Advantages
- high break resistance
- impact strength
- excellent weatherability
- high surface hardness
- abrasion resistance
- very good flow properties
Other Applications
for extrusion of sheets and profiles
injection molding
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Processing Temperature | 220 - 260 | ºC | Barrel Temperature |
Appearance Properties | |||
Refractive index | 1.49 | ISO 489 | |
Physical Properties | |||
MFI | 4.872 | g/10min | ISO 1133@Load 3.80 kg,Temperature 230 °C |
Density | 1.16 | g/ml | ISO 1183 |
Melting range | 220 - 260 | ºC | |
Thermal Properties | |||
Flameability | IEC 707@Thickness 1.60 mm | ||
Vicat softening temperature | 94.0 | ºC | B50; ISO 306 |
Thermal Expansion | 110 | µm/m-°C | ASTM E831 @Temperature 0.000 -50.0 °C |
Dry Time | 120 - 180 | min | Desiccant-type drier |
Mechanical Properties | |||
Elongation at yield | 5.0 | % | 50mm/min; ISO 527 |
(Charpy Impact Strength(unnotched | 75 | kJ/m² | ISO 179@Temperature 23.0 °C |
Tensile modulus-MD | 1900 | MPa | 1mm/min; ISO 527 |
Elongation at break-MD | 50 | % | ISO 527 |
Tensile Stress at yield-MD | 45.0 | MPa | 50mm/min; ISO 527 |
Chemical Properties | |||
Water absorption | 1.8 | % | Immersion; ISO 62;at Saturation |
Moisture absorption | 0.50 | % | 23°C, 50%; ISO 62; at Equilibrium |
Optical Properties | |||
Transmittance | 91 | % | Transmission Factor; DIN 5036;Visible |
Process Properties | |||
Mold Temperature | 50.0 - 70.0 | ºC | |
Drying Temperature | <85.0 | ºC | Predrying |