الوثائق الفنية
PLEXIGLAS® Resist zk4BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I). Application: Used for extruding and coextruding sheets and profiles as well as for injection molding.
تفاصيل
منتج
المورد
مزايا
- excellent weather resistance
- excellent transmission
- claritybrilliant appearance
- high break resistance
- impact strength
- improved resistance to stress cracking
تطبيقات أخرى
extruding and coextruding sheets and profiles
injection molding
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
Processing Temperature | 220 - 260 | ºC | Barrel Temperature |
خصائص المظهر | |||
Refractive index | 1.49 | ISO 489 | |
الخصائص الفيزيائية | |||
Melting range | 220 - 260 | ºC | |
MFI | 5.31 | g/10min | ISO 1133@Load 3.80 kg,Temperature 230 °C |
Density | 1.18 | g/ml | ISO 1183 |
الخصائص الحرارية | |||
Flameability | IEC 707@Thickness 1.60 mm | ||
Heat Deflection temperature | 95.0 | ºC | ISO 75; at 1.8 MPa |
Vicat softening temperature | 102 | ºC | B50; ISO 306 |
Heat Deflection temperature | 99.0 | ºC | ISO 75; at 0.46 MPa |
Thermal Expansion | 80.0 | µm/m-°C | ASTM E831 @Temperature 0.000 -50.0 °C |
Glass transition Temperature | 108 | ºC | IEC 10006 |
Dry Time | 120 - 180 | min | Desiccant-type drier |
خصائص ميكانيكية | |||
(Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179@Temperature 23.0 °C |
Elongation at yield | 4.5 | % | 50mm/min; ISO 527 |
Tensile modulus-MD | 2800 | MPa | 1mm/min; ISO 527 |
Elongation at break-MD | 19 | % | ISO 527 |
Tensile Stress at yield-MD | 71.0 | MPa | 50mm/min; ISO 527 |
الخواص الكيميائية | |||
Water absorption | 2.0 | % | Immersion; ISO 62;at Saturation |
Moisture absorption | 0.60 | % | 23°C, 50%; ISO 62; at Equilibrium |
الخواص البصرية | |||
Transmittance | 92 | % | Transmission Factor; DIN 5036;Visible |
Haze | <1.5 | % | ASTM D1003 |
خصائص العملية | |||
Mold Temperature | 50.0 - 70.0 | ºC | |
Drying Temperature | <90.0 | ºC | Predrying |
اتصل بالمورد