Plexiglas® zk4BR Molding Compound

کمیت	مقدار	واحد	توضیحات

Processing Temperature	220 - 260	ºC	Barrel Temperature
خواص ظاهری
Refractive index	1.49		ISO 489
خواص فیزیکی
Melting range	220 - 260	ºC
MFI	5.31	g/10min	ISO 1133@Load 3.80 kg,Temperature 230 °C
Density	1.18	g/ml	ISO 1183
خواص حرارتی
Flameability	HB		IEC 707@Thickness 1.60 mm
Heat Deflection temperature	95.0	ºC	ISO 75; at 1.8 MPa
Vicat softening temperature	102	ºC	B50; ISO 306
Heat Deflection temperature	99.0	ºC	ISO 75; at 0.46 MPa
Thermal Expansion	80.0	µm/m-°C	ASTM E831 @Temperature 0.000 -50.0 °C
Glass transition Temperature	108	ºC	IEC 10006
Dry Time	120 - 180	min	Desiccant-type drier
خواص مکانیکی
(Charpy Impact Strength(unnotched	25	kJ/m²	ISO 179@Temperature 23.0 °C
Elongation at yield	4.5	%	50mm/min; ISO 527
Tensile modulus-MD	2800	MPa	1mm/min; ISO 527
Elongation at break-MD	19	%	ISO 527
Tensile Stress at yield-MD	71.0	MPa	50mm/min; ISO 527
خواص شیمیایی
Water absorption	2.0	%	Immersion; ISO 62;at Saturation
Moisture absorption	0.60	%	23°C, 50%; ISO 62; at Equilibrium
خواص نوری
Transmittance	92	%	Transmission Factor; DIN 5036;Visible
Haze	<1.5	%	ASTM D1003
خواص فرایندی
Mold Temperature	50.0 - 70.0	ºC
Drying Temperature	<90.0	ºC	Predrying

برای تماس با تامین کنندگان این ماده و ثبت درخواست جهت دریافت قیمت، نمونه، مشاوره و یا پیش فاکتور لطفا فرم درخواست را تکمیل نمایید.

نام و نام خانوادگی

شماره همراه

ایمیل

نام شرکت

زمینه فعالیت

سمت

محل فعالیت

تلفن

وبسایت

در فرآیند تولید نهایی چه میزان از این محصول مورد نیاز می باشد؟

هدف پروژه

نوع پروژه

اطلاعات تکمیلی درخواست